Delo Katiobond 4594 Light-activated adhesive high-viscous 600g

Base

• modified epoxy resin
• one-component, solvent-free, light-activated, thixotropic

Use

• especially for rigid bondings and sealings for example for the fixing of coil wires and components
• for the bonding of metal, glass, plastic and other materials as well as for the coating, fixing or sealing of electronic components
• also suitable for the bonding of opaque components through preactivation
• the cured product is normally used in a temperature range of -40 °C to +150 °C; depending on
• the application, other limits may be more reasonable
• positively tested according to UL 94 HB
• compliant with RoHS directive 2015/863/EU
• halogen-free according to IEC 61249-2-21

Processing

• the product is supplied ready for use; in case of cool storage, it must be ensured that the
• container is conditioned to room temperature before use
• the containers are conditioned at room temperature (max. 25 °C); additional heat addition is not allowed
• the adhesive is usually applied by dispensing
• the adhesive can be processed well from the original container or with DELO dispensing units
• the surfaces to be bonded must be dry as well as free of dust, grease and other contaminations
• use DELOTHEN cleaners for the cleaning of bonding surfaces
• when using aqueous cleaners with alkaline properties, they must be removed from the bonding surface after cleaning through appropriate rinsing cycles
• dispensing valves and product-bearing elements must be carefully cleaned before use,
• residues of other products must be completely removed; acetone or DELOTHEN EP are recommended as cleaners
• for further information please refer to our instructions for use DELO KATIOBOND.

Curing

• curing with UV light or visible light in a wavelength range of 320 – 550 nm. DELOLUX LED
• curing lamps are especially suitable as per the chart below. All standard DELOLUX HID
• discharge lamps are also suitable. For preactivation, only visible light in a wavelength range of 400 – 550 nm can be used.
• the cationic curing mechanism enables adhesive curing after the joining of opaque components after sufficient irradiation
• after irradiation curing until final strength within 24 h at room temperature
• increased temperatures accelerate the reaction, lower temperature decelerate it
• increased intensities shorten the required irradiation time, lower intensities prolong it

Technical specifications

DELO KATIOBOND EG 6133, ​DELO KATIOBOND EG-6133

DELO Industrie Klebstoffe GmbH & Co. KGaA, DELO-Allee 1, 86949 Windach, GERMANY, +49 8193 9900-0, [email protected], www.delo.de